ASTALOY™ PC/ABS MDA216
丙烯腈丁二烯苯乙烯+聚碳酸酯

Marplex Australia Pty. Ltd.

产品说明

ASTALOY™ MDA216 is a high melt flow specialty mineral filled alloy of ABS and Polycarbonate which is designed for long flow path injection moulding applications requiring a balance of impact toughness, product rigidity, dimensional stability over a broad temperature range, high heat resistance and mouldability. Typical automotive applications include painted exterior body panels, structural instrument panel mounting substrates and painted front/rear air deflectors.

Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ MDA216-U ].

总体

材料状态 • 已商用：当前有效   
供货地区 • 北美洲 • 南美洲 • 亚太地区 
填料/增强材料 • 矿物填料   
性能特点 • 尺寸稳定性良好 • 流动性高 • 中等硬度 
 • 抗撞击性，良好 • 适于粉刷  
    
用途 • 汽车领域的应用： • 汽车外部零件 • 汽车仪表板 
加工方法 • 注射成型   

物理性能  额定值单位制 测试方法
比重  1.16g/cm³ ASTM D792
熔流率 (250°C/3.8 kg) 11g/10 min ASTM D1238
收缩率 - 流动 (3.00 mm) 0.40 到 0.80% ASTM D955
吸水率 (24 hr) 0.25% ASTM D570
机械性能  额定值单位制 测试方法
抗张强度 2 (3.20 mm) 59.0MPa ASTM D638
伸长率 2 (断裂, 3.20 mm) 80% ASTM D638
弯曲模量 3 (3.20 mm) 2850MPa ASTM D790
弯曲强度 3 (3.20 mm) 92.0MPa ASTM D790
冲击性能  额定值单位制 测试方法
悬壁梁缺口冲击强度 (3.20 mm) 600J/m ASTM D256
落锤冲击 (3.20 mm) 60.0J ASTM D3029
硬度  额定值单位制 测试方法
洛氏硬度 (R 计秤) 116 ASTM D785
热性能  额定值单位制 测试方法
热变形温度  ASTM D648
1.8 MPa, 未退火, 3.20 mm 105°C 
1.8 MPa, 未退火, 6.40 mm 110°C 
1.8 MPa, 未退火, 12.7 mm 114°C 
维卡软化温度 138°C ASTM D1525 4
线形膨胀系数 - 流动 0.000050cm/cm/°C ASTM D696
可燃性  额定值单位制 测试方法
UL 阻燃等级 (1.60 mm) HB UL 94
热灯丝点火温度 (1.60 mm) 550°C AS/NZS 60695.2.12
   
注射  额定值单位制 
干燥温度  100 到 110°C 
干燥时间  3.0 到 5.0hr 
螺筒后部温度 235 到 255°C 
螺筒中部温度 245 到 265°C 
螺筒前部温度 255 到 275°C 
加工（熔体）温度 250 到 280°C 
模具温度  50.0 到 90.0°C 
注塑温度  60.0 到 140MPa 
注射速度  中等 
背压  0.100 到 0.500MPa 
螺杆转速  40 到 60rpm 
 
ASTALOY™ PC/ABS MDA216 2012年9月25日
丙烯腈丁二烯苯乙烯+聚碳酸酯 
Marplex Australia Pty. Ltd. 
注射 额定值单位制
合模力 4.0 到 8.0kN/cm²

备注
1 一般属性：这些不能被视为规格。

2 5.0 mm/min

3 1.3 mm/min

4 压 力1 (10N)