Jamplast JPPCABSI
丙烯腈丁二烯苯乙烯+聚碳酸酯
Jamplast, Inc. 

Technical Data

产品说明

JPPCABSI engineering resin is designed to offer a balance of properties between impact strength, heat resistance and processability. It offers better processability than polycarbonate while offering high impact strength at both room and low temperatures compared to ABS. With a deflection temperature under load (264 psi, unannealed) of 230°F, JPPCABSI also offers high heat resistance compared to ABS. JPPCABSI engineering resin has been used in automotive instrument panel and interior trim applications.

总体

材料状态 • 已商用：当前有效  
供货地区 • 北美洲  
形式 • 颗粒料  
加工方法 • 共挤出成型 • 片材挤出成型 • 注射成型

物理性能 额定值单位制 测试方法
比重 1.13g/cm³ ASTM D792
熔流率 (230°C/3.8 kg) 3.0g/10 min ASTM D1238
收缩率 - 流动 0.70% ASTM D955
吸水率  ASTM D570
23°C, 24 hr 0.15% 
平衡, 23°C, 50% RH 0.32% 
机械性能 额定值单位制 测试方法
抗张强度 2  ASTM D638
屈服 53.1MPa 
断裂 44.8MPa 
伸长率 2 (断裂) 130% ASTM D638
弯曲模量 2340MPa ASTM D790
弯曲强度 (屈服) 82.7MPa ASTM D790
冲击性能 额定值单位制 测试方法
悬壁梁缺口冲击强度 3  ASTM D256
-40°C, 3.18 mm 430J/m 
-29°C, 3.18 mm 530J/m 
23°C, 3.18 mm 730J/m 
装有测量仪表的落镖冲击 4  ASTM D3763
-29°C, 3.18 mm, Total Energy 62.1J 
23°C, 3.18 mm, Total Energy 56.5J 
硬度 额定值单位制 测试方法
洛氏硬度 (R 计秤) 115 ASTM D785
热性能 额定值单位制 测试方法
热变形温度  ASTM D648
1.8 MPa, 未退火, 3.18 mm 110°C 
1.8 MPa, 退火, 3.18 mm 121°C 
线形膨胀系数 - 流动 (-40 到 82°C) 0.000074cm/cm/°C ASTM D696

备注
1 一般属性：这些不能被视为规格。

2 类型 1, 51 mm/min

3 0.25 mm 缺口深度

4 3.39 m/sec