共挤出成型，片材挤出成型

Jamplast JPPCABSI

聚碳酸酯+丙烯腈丁二烯苯乙烯

Jamplast, Inc.

Technical Data

 

产品说明

JPPCABSI engineering resin is designed to offer a balance of properties between impact strength, heat resistance and processability. It offers better processability than polycarbonate while offering high impact strength at both room and low temperatures compared to ABS. With a deflection temperature under load (264 psi, unannealed) of 230°F, JPPCABSI also offers high heat resistance compared to ABS. JPPCABSI engineering resin has been used in automotive instrument panel and interior trim applications.

 

总体

 

材料状态 • 已商用：当前有效

 

供货地区 • 北美洲

 

形式 • 粒子

 

加工方法 • 共挤出成型 • 片材挤出成型 • 注射成型

 

物理性能 额定值单位制 测试方法

密度 / 比重 1.13g/cm³ ASTM D792

熔流率（熔体流动速率） (230°C/3.8 kg) 3.0g/10 min ASTM D1238

收缩率 - 流动 0.70% ASTM D955

吸水率 ASTM D570

24 hr, 23°C 0.15%

平衡, 23°C, 50% RH 0.32%

机械性能 额定值单位制 测试方法

抗张强度 2 ASTM D638

屈服 53.1MPa

断裂 44.8MPa

伸长率 2 (断裂) 130% ASTM D638

弯曲模量 2340MPa ASTM D790

弯曲强度 (屈服) 82.7MPa ASTM D790

冲击性能 额定值单位制 测试方法

悬壁梁缺口冲击强度 3 ASTM D256

-40°C, 3.18 mm 430J/m

-29°C, 3.18 mm 530J/m

23°C, 3.18 mm 730J/m

装有测量仪表的落镖冲击 4 ASTM D3763

-29°C, 3.18 mm, Total Energy 62.1J

23°C, 3.18 mm, Total Energy 56.5J

硬度 额定值单位制 测试方法

洛氏硬度 (R 级) 115 ASTM D785

热性能 额定值单位制 测试方法

载荷下热变形温度 ASTM D648

1.8 MPa, 未退火, 3.18 mm 110°C

1.8 MPa, 退火, 3.18 mm 121°C

线形热膨胀系数 - 流动 (-40 到 82°C) 7.4E-5cm/cm/°C ASTM D696

 

 

 

 

 

 

Jamplast, Inc.聚碳酸酯+丙烯腈丁二烯苯乙烯,Jamplast, Inc. PC+ABS,PC+ABS Jamplast JPPCABSI塑料是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，ROHS报告，REACH报告  SVHC报告，COA出厂报告,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123  微信：13549213581     联系电话：13549213581肖生